Main Page
About
Faculty
Dean
Organizational Structure
Academic Accreditations
"Strategic Plan "Ebtesama-Smile
Administration
Vice Deanships
Academic Affairs
Female Section
Graduate Studies and Research
University Dental Hospital
Development
Departments
Diagnostic Oral Sciences
Periodontology
Oral Biology
Oral & Maxillofacial Prosthodontics
Oral & Maxillofacial Surgery
Endodontics
Restorative Dentistry
Orthodontics
Pediatric Dentistry
Dental Public Health
Goals and Objectives
Education
Bachelor
Interns Program
Postgraduate Studies
Research
University Dental Hospital
Community Services
House of Expertise
Files
Contact Us
Directory of Faculty Staff
عربي
English
About
Admission
Academic
Research and Innovations
University Life
E-Services
Search
Faculty of Dentistry
Document Details
Document Type
:
Article In Journal
Document Title
:
SHEAR BOND STRENGTH OF CHEMICALLY CURED GLASS
SHEAR BOND STRENGTH OF CHEMICALLY CURED GLASS
Document Language
:
English
Abstract
:
Conditioning of dentin prior to placement of chemically cured glass ionomer cement (GIC) still represents a controversial issue for most of the clinicians. The purpose of this in vitro study was to evaluate the effect of three dentin pretreatment (water rinsing and dryness, 25% polyacrylic acid and mixed solution of 10% citric acid and 3% ferric chloride) on the shear bone strength of two commercial capsulated chemically cured glass ionomer restoratives (Ketac-Fil & Ketac–Silver). Representative samples of the different treatment groups were submitted for SEM before bonding with GIC to visually assess the resultant dentin surface morphologies. Bond strength to the control group ranged from 3.47 ± 0.54 MPa for Ketac-Fil and from 5.32 ± 0.67 MPa for Ketac-Silver. Conditioning with 25% polyacrylic acid resulted in bond strength ranged from 3.62 ± 0.61 MPa for Ketac-Fil and from 5.64 ± 0.55 MPa for Ketac-Silver. Treatment of dentin with a mixed solution of 10% citric acid and 3% ferric chloride resulted in bond strength ranged from 4.69 ± 0.78 MPa for Ketac-Fil and from 7.00 ± 0.84 MPa for Ketac-Silver. It was concluded that, the polyacrylic acid dentinal pretreatment did not enhance the bond strength of GIC to dentin significantly when compared to the untreated control group. Moreover, the mixed solution of 10% citric acid and 3% ferric chloride caused aggressive etching of the dentin as seen under the SEM, but it resulted in the highest improvement in the shear bond strength of GIC to dentin among all the tested groups. Finally, longitudinal biological and clinical studies on the effects of citric acid and ferric chloride dentinal pretreatment are recommended before being advocated for use with chemically cured GIC. * Lecturer of Operative Dentistry, Faculty of Oral and Dental Medicine, Cairo University ** Lecturer of Dental Bio-Materials, Faculty of Oral and Dental Medicine, Cairo University
ISSN
:
0
Journal Name
:
Egyptian Dental Journal
Volume
:
46
Issue Number
:
1
Publishing Year
:
2000 AH
2000 AD
Article Type
:
Article
Added Date
:
Saturday, May 3, 2008
Researchers
Researcher Name (Arabic)
Researcher Name (English)
Researcher Type
Dr Grade
Email
مصطفى حسان
hassan, mostafa
Investigator
Doctorate
mahassan2@kau.edu.sa
Files
File Name
Type
Description
SHEAR BOND STRENGTH OF CHEMICALLY CURED GLASS.pdf
pdf
Back To Researches Page